Polishing suspension based on the silica dioxide
It is meant for a
finishing polish of optic and electronic products. In particular, it is used
at the stage of finishing polish of silicon mono-crystal plates.
It is an ultra-disperse colloid system based on silicon dioxide. It is a liquid of the co lour
of the milk without any visible mechanical inclusions.
It possesses a polishing capability for optic
and electronic products at a normal speed of a material lift.
Admixture
|
Type of suspension
|
SPS - 55
|
SPS - 53
|
SPS - 8
|
SPS - 81
|
SPS - 54
|
Iron
|
0,0002
|
0,0002
|
0,0002
|
0,00002
|
0,0003
|
Sodium
|
0,4
|
0,4
|
0,0005
|
0,00005
|
0,0004
|
Potassium
|
0,00005
|
0,00005
|
0,0004
|
0,00004
|
0,00004
|
Stabilizing base
|
NaOH, KOH
|
NaOH, KOH
|
Ethylendiamin
|
Ethylendiamin
|
-
|
Density, g/cm3
|
1,130-1,134
|
1,060-1,065
|
1,075-1,080
|
1,10-1,12
|
1,10-1,12
|
рН at 200С
|
9,5-10,9
|
9,5-10,9
|
11,8-12,0
|
12,5-12,8
|
5,5-7,0
|
Size of particles of SiO2, nm
|
50-100
|
10-40
|
10-40
|
50-100
|
50-100
|
Content of
SiO2, mass %
|
20,0
|
10,0
|
12,5
|
20,0
|
16,0
|
Appearance of suspension
|
Milk color liquid
|
Milk color liquid
|
Milk color liquid
|
Milk color liquid
|
Milk color liquid
|
Viscosity, MPas
|
1,8
|
1,25
|
1,25
|
1,7
|
1,7
|
Stage of usage
|
II stage
|
II stage
|
I stage
|
I stage
|
-
|
Recommended dilution
|
1:10
|
1:5
|
1:3
|
1:5
|
|
рН after dilution
|
10,5-10,6
|
10,5-10,6
|
11,8-11,9
|
12,2-12,3
|
-
|
Density after dilution, g/cm3
|
1,010
|
1,010
|
1,015
|
1,010
|
-
|
Recommended type of polishing
|
segal or polyvel
|
segal
|
polytan
|
polytan
|
segal, polyvel, polytan and e.a.
|
Serviceable life, months, at
least
|
6
|
6
|
6
|
6
|
6
|
|